Products Description
TP310S Stainless Steel Tube is a high-alloy austenitic stainless steel seamless tube, mainly composed of high content of chromium and nickel content.
Product Parameters
|
Product Name |
ASTM A213 TP310S Stainless Steel Tube |
|
Out Diameter |
10-219mm |
|
Wall Thickness |
0.5-60mm |
|
Material Standard |
ASTM A213 |
|
Steel Grade |
ASTM A213 TP310S |
|
Surface |
Pickling, Solid solution, Polishing |
|
Packing |
Plastic Film, Plastic Cap, Bundle, Woven bag, Wooden Case, Iron Frame |
|
Delivery |
Within 3 days with stock, 15-50 days based on production |
|
Payment |
T/T, D/P, L/C at sight, Usance L/C, etc. |
Chemical Requirements
|
Grade |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
|
TP310S |
0.08max |
2.00max |
0.045max |
0.030max |
1.00max |
24.00-26.00 |
19.00-22.00 |
Mechanical Property
|
Grade |
Tensile strength Min Ksi(Mpa) |
Yield strength Min Ksi(Mpa) |
Elongation % min |
Hardness |
|
|
Brinell/Vickers |
Rockwell |
||||
|
TP310S |
75(515) |
30(205) |
35 |
192HBW/200HV |
90HRB |
Advantages
Strong thermal shock stability
Compared to 304 and 316 stainless steel, the austenitic structure of TP310S is more resistant to thermal shock microcracks caused by rapid temperature changes, making it suitable for frequent temperature fluctuations, thereby ensuring equipment safety and reducing downtime.
Excellent high-temperature resistance
TP310S Stainless Steel Tube contains a high chromium and high nickel alloy, and a dense oxide film is formed on the surface, ensuring that the pipe can operate stably in a high-temperature environment above 1000℃ for a long time.
Excellent mechanical strength
This product complies with the smelting and heat treatment process of ASTM A213 standard, ensuring a tensile strength of≥ 515 MPa, which meets the requirements of high-temperature and high-pressure conditions.
Product Show
To meet market demand, our company offers a variety of stainless steel tubes, including stainless steel industrial seamless tubes, stainless steel welded tubes, stainless steel boiler tubes, stainless steel capillary tubes, stainless steel bright tubes, and sanitary stainless steel tubes.
Product Packing
Polished stainless steel tubes should be individually wrapped with plastic film before bundling. Cold-drawn or cold-rolled stainless steel tubes should be tightly wrapped with no less than two layers of sack cloth, braided tape, or plastic cloth before bundling. Protective material should be used between the stainless steel tube and the steel strip or wire.
Why Choose us
Company Strength
Hebei Yongqiang Pipeline Co., Ltd. is a professional steel pipe supplier integrating R&D, production, and sales. Its products include austenitic stainless steel pipes, duplex stainless steel pipes, alloy steel pipes, casing steel pipes, steel pipe accessories, steel flanges, etc.
Sales Market: Our company's business covers the Middle East, North Africa, South America, Southeast Asia, Central America, and other regions, with an annual export volume of more than 10 million US dollars.
Our Products: We provide a range of high-quality steel products, including austenitic stainless steel pipes, alloy steel pipes, casing steel pipes, and steel flanges. These products are designed to meet various industrial needs.
Our Services: Our company can provide 24-hour service to negotiate product parameters, prices, delivery dates, transportation, and other details with customers.
- We have excellent sales personnel and technicians who can quickly and effectively resolve your issues.
- We have the complete production capacity to meet your delivery requirements.
- Over the years, we have maintained strong and close cooperation with major steel tube manufacturers and distributors in China, allowing us to meet various customer needs. To ensure product quality, we can engage third-party organizations for product testing.
- We provide secure and comprehensive packaging services to prevent loss of goods during transportation, especially for ocean shipments.
For inquiries about ASTM A213 TP310S stainless steel tubes, please contact us, and we will respond within one hour.
Email: johnny@yqtubeline.com
WhatsApp: +86 15632733100
Tel: +86 317 6376727
FAQ
Q: What is a TP310S Stainless Steel Tube?
A: ASTM A312 310s is a material used for general corrosive services and high temperature services for prolonged periods. The composition of the A312 TP310s material includes carbon, manganese, silicon, phosphorus, sulfur, chromium, and nickel.
Q: How does TP310S stainless steel differ from other grades of stainless steel?
A: The addition of nickel and chromium makes 310s highly resistant to oxidation and corrosion, even in environments exposed to high temperatures and harsh conditions. This grade is particularly noted for its excellent resistance to sulfidation and can be used in moderately carburizing atmospheres.
Q: In what industries is TP310S Stainless Steel Tube commonly used?
A: The austenitic heat-resistant alloy helps the stainless steel 310s grade pipes prevent oxidation and corrosion under extremely high temperatures, hence used in heat treatment and Process industries.
Q: What is the chemical composition of TP310S Stainless Steel Tube?
A: The composition of the A312 Tp310s material includes carbon, manganese, silicon, phosphorus, sulfur and chromium, and nickel. The composition makes the material withstand highly oxidizing agents under high temperatures.
Q: What are the advantages of using TP310S Stainless Steel Tube over carbon steel pipes?
A: The composition of the A312 Tp310s material includes carbon, manganese, silicon, phosphorus, sulfur and chromium, and nickel. The composition makes the material withstand highly oxidizing agents under high temperatures.
Q: Can TP310S Stainless Steel Tube withstand high temperatures?
A: The 310S has lower carbon content at 0.08% max, where the 310 has 0.24% max of carbon. The material is used for high temperature services with 1150 degrees Celsius at continuous services and 1035 degrees Celsius with intermittent services. It has corrosion resistance and high forming abilities.
Q: Is TP310S Stainless Steel Tube resistant to corrosion?
A: The 310S has lower carbon content at 0.08% max, where the 310 has 0.24% max of carbon. The material is used for high temperature services with 1150 degrees Celsius at continuous services and 1035 degrees Celsius with intermittent services. It has corrosion resistance and high forming abilities.
Q: What inspection and testing methods are recommended for TP310S Stainless Steel Tube?
A: Testing of Stainless Steel Tubes – All ASTM A312 TP310 stainless steel pipes are subjected to hydrostatic test, eddy current test, chemical, and mechanical tests during the various stages of production.
Q: Are there any ASTM standards applicable to TP310S Stainless Steel Tube?
A: ASTM A249 310S Welded Condenser Tubes are being designed as per the national and international standard quality of raw materials. ASTM A249 SS 310S Tubing has a maximum dry air service temperature of 1100ºC. Also referred to as WNR 1.4845 Welded Tube.
Q: What is the tensile strength of TP310S Stainless Steel Tube?
A: The 310s material also has a high minimum yield strength of 205MPa and a minimum tensile strength of 525MPa. This allows the materials to be used under high pressure as well.
Hot Tags: tp310s stainless steel tube, China tp310s stainless steel tube manufacturers, suppliers, factory, TP347 Stainless Steel Pipe, high purity stainless steel tubing, stainless steel precision tube, cold drawn stainless steel tube, mirror polished stainless steel tubing, TP304H Stainless Steel Tube